Effects of Al on the magnetic properties of nanocrystalline Fe 73.5Cu1Nb3Si13.5B9 alloys

S. H. Lim, W. K. Pi, T. H. Noh, H. J. Kim, I. K. Kang

Research output: Contribution to journalArticlepeer-review

27 Citations (Scopus)


The effects of Al on the soft magnetic properties of nanocrystalline Fe73.5-xAlxCu1Nb3Si 13.5B9 alloy ribbons are investigated in the composition range of 0≤x≤1.0. The relative initial permeability at 1 kHz is found to increase by the addition of Al, and reaches the peak value at x=0.1. The coercivity decreases, rather significantly, with the Al content in the whole composition range investigated in the present work, the values of the coercivity being 12.5 mOe at x=0 and 9.3 mOe at x=1.0. The magnetic induction at an applied field of 10 Oe, however, decreases moderately by the introduction of Al, possibly due to the dilution effect. The improvement in the soft magnetic properties is considered to result from the reduction in the grain size of the α Fe-Si solid solution phase of the Al-added alloy ribbons, which has been observed by transmission electron microscopy. Another factor may be due to the decrease in the intrinsic magnetocrystalline anisotropy K1 as Al is added to the alloy.

Original languageEnglish
Pages (from-to)6591-6593
Number of pages3
JournalJournal of Applied Physics
Issue number10
Publication statusPublished - 1993
Externally publishedYes

ASJC Scopus subject areas

  • Physics and Astronomy(all)


Dive into the research topics of 'Effects of Al on the magnetic properties of nanocrystalline Fe 73.5Cu1Nb3Si13.5B9 alloys'. Together they form a unique fingerprint.

Cite this