Uncommon low loss Mg1•5Zn0•5SiO4 ceramics containing Bi2O3 were investigated by focusing on the roles of Bi2O3 on phase evolution and resultant microwave dielectric properties. While the primary goal of lowering sintering temperature can be easily assumed, some unexpected behaviours of the Bi 2O3 containing materials are highlighted with experimental evidences concerning selective dissolution of Zn2SiO4 and grain boundary segregation of gradual Bi richer phases. These evidences are strongly dependent on the content of Bi2O3 and sintering temperature. As an optimal composition, Mg1•5Zn 0•5SiO4 with 0•5?mol.-%Bi2O 3 exhibited promising dielectric properties of a k value ∼6•8 and a Q×f value ∼23∈300 at a sintering temperature of 1150°C, which is much lower than typical sintering temperature of 1450°C.
|Number of pages||6|
|Journal||Advances in Applied Ceramics|
|Publication status||Published - 2010 Aug 1|