Piezoelectric properties of PZT-based ceramic with highly aligned pores

Seung Ho Lee, Shin Hee Jun, Hyoun Ee Kim, Young Hag Koh

Research output: Contribution to journalArticlepeer-review

58 Citations (Scopus)


Porous lead zirconate titanate-lead zinc niobate (PZT-PZN) piezoelectric ceramics with a high degree of pore alignment were fabricated using directional freeze casting of a ceramic/camphene slurry. Well-aligned pores were formed as the replica of the camphene dendrites that grew in a preferential orientation, while a high porosity of 90% was achieved by employing a low initial solid loading of 5 vol%. As the orientation angle of the pores to the poling direction was decreased, the hydrostatic piezoelectric properties, such as hydrostatic piezoelectric strain coefficient (dh), the hydrostatic piezoelectric voltage coefficient (gh), and the hydrostatic figure of merit, increased significantly. The sample containing pores aligned parallel to the poling direction showed an extremely high HFOM of 161019 × 10 -15 Pa-1, which was ∼1300 times higher than that (124 × 10-15 Pa-1) of the dense sample, owing to the presence of aligned pores.

Original languageEnglish
Pages (from-to)1912-1915
Number of pages4
JournalJournal of the American Ceramic Society
Issue number6
Publication statusPublished - 2008 Jun

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry


Dive into the research topics of 'Piezoelectric properties of PZT-based ceramic with highly aligned pores'. Together they form a unique fingerprint.

Cite this