The oxidation of SiC particles and its interfacial characteristics in Al-matrix composite

Zhongliang Shi, Shojiro Ochiai, Masaki Hojo, Jaechul Lee, Mingyuan Gu, Hoin Lee, Renjie Wu

Research output: Contribution to journalArticlepeer-review

30 Citations (Scopus)


The passive oxidation behavior of SiC particles has been studied in an electric furnace at atmospheric pressure and in dry air, the weight change due to the transformation from SiC into SiO2 is descibed as a function of exposed temperature and holding time. According to the oxidation data of SiC particles, the oxidation parameters and the degree of oxidation for SiC particles can be controlled. Controllable preoxidation of SiC particles is one of the keys for designing interface and interphase to achieve high performance aluminum composite. Consequently, the evolution of interfacial reaction products in 2014 aluminum alloy composite reinforced with oxidized-SiC particles after extended thermal exposure at elevated temperatures were further characterized by Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), and X-ray diffraction. While it could act to prevent the interfacial reaction between SiC particles and aluminum alloy, the preoxidation of SiC particles led to the formation of other interfacial reaction products. The observation of the microstructure revealed that at elevated temperatures nano-MgO formed initially on the surface of the oxidized SiC particles and then turned into nano-MgAl2O4 crystal due to the reaction between the SiO2 and aluminum alloy containing Mg. TEM observations indicated that the oxidized layer on SiC particles was uniform and had a good bonding with SiC and aluminum alloy.

Original languageEnglish
Pages (from-to)2441-2449
Number of pages9
JournalJournal of Materials Science
Issue number10
Publication statusPublished - 2001 May 15
Externally publishedYes

Bibliographical note

Funding Information:
Zhongliang Shi is grateful for the supports from the National Nature Science Foundation of P.R. China grant No. 59631080 and the Science and Technology Policy Institute of Korea (STEPI) as a visiting scientist at Korea Institute of Science and Technology and Japan Society for the Promotion of Science as a JSPS fellow at Kyoto University.

ASJC Scopus subject areas

  • General Materials Science
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'The oxidation of SiC particles and its interfacial characteristics in Al-matrix composite'. Together they form a unique fingerprint.

Cite this